Haynes 25(AlloyL605) is a solid solution strengthened cobalt-chromium-tungsten nickel alloy with excellent high -temperature strength and excellent oxidation resistance to 2000°F(1093°C). The alloy also offers good resistance to sulfidation and resistance to wear and galling. Alloy L-605 is useful in gas turbine applications such as rings,blades and combustion chamber parts (sheet fabrications) and can also can be used in industrial furnace applications such as muffles or liners in high temperature kilns.
|Specific heat capacity
Representative Tensile Properties, Sheet
|Ultimate Tensile Strength, ksi||146||108||93||60||34|
|0.2% Yield Strength, ksi||69||48||41||36||18|
Typical Stress-Rupture Strength
|100 Hours, ksi||69||36||25||18||12||7|
|1,000 Hours, ksi||57||26||18||12||7||4|
AMS 5537, AMS 5796,EN 2.4964,GE B50A460,UNS R30605,Werkstoff 2.4964
|AMS 5537||AMS 5537||--|
Round bars/Flat bars/Hex bars, Size From 8.0mm-320mm, Used for bolts,fastners and other spare parts
Supply in welding wire and spring wire in coil form and cut length.
Widths up to 1500mm and lengths up to 6000mm,Thickness from 0.1mm to 100mm.
Dimension can be customized with bright surface and precision tolerance.
Soft condition and hard condition with AB bright surface, width up to 1000mm
• Outstanding high temperature strength
• Oxidation resistant to 1800°F
• Galling resistant
• Resistant to marine environments, acids and body fluids
• Gas turbine engine components such as combustion chambers and afterburners
• High temperature ball bearings and bearing races
• Heart valves